- Approvals: DNV-GL TAS00002XE
- Height: 20.6 mm
- Material thickness: 2 mm
- Approvals: Shock approved (LS-S-06-904), DNV-GL TAS00002XE
- Height: 41.3 mm
- Material thickness: 2 mm
- Height: 82.6 mm
- Material thickness: 2 mm
- Material composition: S250GD - DIN EN 10346
- Height: 82.6 mm
- Material thickness: 2 mm
- Material composition: S235JR - DIN EN 10025
- Height: 52 mm
- Material thickness: 2.5 mm
- Material composition: S235JR - DIN EN 10025
- Height: 124 mm
- Material thickness: 2.5 mm, 2.75 mm
- Material composition: S250GD - DIN EN 10346
- Height: 72 mm
- Material thickness: 2.75 mm
- Material composition: S235JR - DIN EN 10025
- Height: 124 mm
- Material thickness: 3 mm
- Material composition: S250GD - DIN EN 10346
- Material thickness: Channel: 2 mm, Baseplate: 6 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: Channel: 2 mm, Baseplate: 8 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: Channel: 2 mm, Baseplate: 8 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: Channel: 2 mm, Baseplate: 10 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Approvals: VDS approved G4970048
- Material thickness: Channel: 2.75 mm, Baseplate: 10 mm
- Material composition: S235JR - DIN EN 10025
- Approvals: DNV-GL TAS00002XE
- Material thickness: 3 mm
- Material composition: S235JR - DIN EN 10025
- Tightening torque: 25 Nm
- Material composition: Plate: steel S355J2 DIN EN 10025-2, Nut: S355MC - DIN EN 10149-2, Bolt: grade 8.8 - DIN EN ISO 898
- Surface finish: Multi-layer coating – performance in salt spray test equal to hot-dip galvanizing
- Material composition: Nut: EN-GJMW-450-7 - DIN EN 1562, Plate: S235JR - DIN EN 10025, Plastic: PB
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- For use with: MQ channels
- Tightening torque: 40 Nm
- Thread connection - M: M12
- Material composition: Wings: plastic PA, Nut: C4C - DIN EN 10263
- Tightening torque: 20 Nm
- Thread connection - M: M8
- Material composition: Wings: plastic PA, Nut: QStE 380 TM, SEW 92
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Approvals: DNV-GL TAS00002XE
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Approvals: DNV-GL TAS00002XE
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Approvals: Shock approved (LS-S-06-904), DNV-GL TAS00002XE
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Weight: 420 g
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: U-bolt: S235JRG2 - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Wrench size: 17 mm
- Tightening torque: 40 Nm
- Material composition: DD11 MOD - HN 547, S235JR - DIN EN 10025, Bolt: M10x10-10.9-HDG - DIN 933
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Weight: 26 g